(R) Lubricant, Solid Film, Heat Cured,
Corrosion Inhibiting
Procurement Specification
MOS2/二硫化鉬
1. SCOPE:
This SAE Aerospace Standard (AS) establishes the requirements for heat cured solid film
lubricants. For other general or high temperature applications, see AS1701.
1.1 Application:
For applications where temperatures may range from -90 to 400 °F (-68 to 204 °C).
1.2 Type:
This specification establishes the following types:
Type I: A lubricant capable of being cured within 60 minutes at 302 °F ± 27 °F (150 °C
± 15 °C) with an endurance life of 250 minutes minimum. See 6.4 for related
product information.
Type II: A lubricant capable of being cured within 60 minutes at 400 °F ± 27 °F (204 °C
± 15 °C) with an endurance life of 450 minutes minimum. See 6.4 for related
product information.
Type III: A low volatile organic compound (VOC) content lubricant capable of being
cured within 120 minutes at 302 °F ± 27 °F (150 °C ± 15 °C) or within
60 minutes at 400 °F ± 27 °F (204 °C ± 15 °C) with an endurance life of
450 minutes minimum. Type III shall be used when performance is satisfactory
for the desired application to meet VOC emission regulations.
Color 1 - Natural product color.
Color 2 - Black color. See 3.7.
See 6.4 for related product information.